Cracking susceptibility after post-weld heat treatment in haynes 282 nickel based superalloy

No Thumbnail Available
Osoba, L.O.
Khan, A.K.
Adeosun, S.O.
Journal Title
Journal ISSN
Volume Title
ACTA Metallurgica Sinica
This paper presents a study of the standard post-weld heat treatment (PWHT) behaviour of autogenous laser welded γ’ age-hardenable precipitation strengthened nickel based superalloy Haynes 282 (HY 282). The study involves a careful and detailed microstructural characterisation as well as an analysis of the weld cracking susceptibility during welding and Gleeble thermo-mechanical physical simulation. Various factors that could influence post-weld cracking in superalloys weld were experimentally examined. Our microstructural examination of the as-solution heat treated (SHTed) material and the thermo-mechanically refined grain material shows that intergranular heat affected zone (HAZ) cracking is observable in only the as-welded SHTed material. There was no indication of post-weld heat treatment cracking in all welded materials. Our conclusion, in this study, is that the chemistry of superalloy HY 282 which aids the preclusion/ formation of deleterious solidification microconstituents during welding as well as its relatively slow aging kinetics enhances its resistance to PWHT cracking.
Staff publications
Cracking , Microstructure analysis , Nickel based superalloy , Heat treatment , Research Subject Categories::TECHNOLOGY
Osoba, L.O., Khan, A.K., Adeosun, S.O., (2013). Cracking susceptibility after post-weld heat treatment in haynes 282 nickel based superalloy, ACTA Metallurgica Sinica, 26(6):747—753