Hot injection thermolysis of heterometallic pivalate clusters for the synthesis of monodisperse zinc and nickel ferrite nanoparticles

Simple item page
dc.contributor.authorAbdulwahab, K.O.
dc.contributor.authorMalik, M.A.
dc.contributor.authorO'Brien, P.
dc.contributor.authorTimco, G.A.
dc.contributor.authorTuna, F.
dc.contributor.authorWinpenny, R.E.
dc.contributor.authorPattrick, R.A.
dc.contributor.authorCoker, V.S.
dc.contributor.authorArenholz, E.
dc.date.accessioned2019-08-26T12:57:53Z
dc.date.available2019-08-26T12:57:53Z
dc.date.issued2014
dc.description.abstractThe heterometallic pivalate clusters- [Zn4Fe2O2(O2CtBu)10] (1) and [Fe2NiO(O2CtBu)6(HO2CtBu)3] (2) have been used as single source precursors to synthesise monodispersed zinc ferrite (ZnFe2O4) and nickel ferrite (NiFe2O4) nanoparticles respectively. The precursors were thermolysed with a mixture of oleylamine and oleic acid in either diphenyl ether or benzyl ether as the solvent at their respective boiling points of 260 and 300 C. The effect of reaction time, temperature and concentration (0.25 or 0.50 mmol) on the stoichiometry, the phase or morphology of the nanoparticles were studied. TEM showed that highly monodispersed spherical nanoparticles of zinc ferrite (3.2 0.2 nm) and nickel ferrite (3.3 0.2 nm) respectively were obtained from (1) and (2) using 0.50 mmol precursor concentration at 260 C. The decomposition of the precursors at 0.25 mmol and 300 C gave larger nanoparticles of zinc ferrite (5.6 0.5 nm) and nickel ferrite (5 0.6 nm) from (1) and (2) respectively. The effect of reaction time was investigated for both precursors at 0.25 mmol by withdrawing aliquots at 5 minutes, 15 minutes, 30 minutes, 1 hour and 2 hours. Aliquots withdrawn at reaction times of less than 1 hour contain traces of iron oxide whilst only pure cubic zinc or nickel ferrite was obtained after one hour. Magnetic measurements revealed that all the ferrite particles are superparamagnetic at room temperature with high saturation magnetisation values. XMCD confirmed that in nickel ferrite particles, most of the Ni2+ cations are in the octahedral site. The hysteresis loop observed on the zinc ferrite nanoparticles indicated that there is cation redistribution, this is further evident in the XMCD analysis and EPMA result.en_US
dc.identifier.citationAbdulwahab, K. O., Malik, M. A., O'Brien, P., Timco, G. A., Tuna, F., Winpenny, R. E., ... & Arenholz, E. (2014). Hot injection thermolysis of heterometallic pivalate clusters for the synthesis of monodisperse zinc and nickel ferrite nanoparticles. Journal of Materials Chemistry C, 2(33), 6781-6789.en_US
dc.identifier.urihttps://ir.unilag.edu.ng/handle/123456789/4736
dc.language.isoenen_US
dc.publisherThe Royal Society of Chemistryen_US
dc.relation.ispartofseries;DOI: 10.1039/c4tc00832d
dc.subjectResearch Subject Categories::NATURAL SCIENCES::Chemistry::Inorganic chemistry::Solid state chemistryen_US
dc.titleHot injection thermolysis of heterometallic pivalate clusters for the synthesis of monodisperse zinc and nickel ferrite nanoparticlesen_US
dc.typeArticleen_US
Files
Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
zinc ni ferrite.pdf
Size:
231.71 KB
Format:
Adobe Portable Document Format
Description:
Abstract
Download
License bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
license.txt
Size:
1.71 KB
Format:
Item-specific license agreed upon to submission
Description:
Download
Collections
Chemistry-Scholarly Publications