Investigation into the Deep Drawability of 0.1%C Eutectoid Steel
dc.contributor.author | Adeosun, S.O. | |
dc.contributor.author | Sekunowo, O.I. | |
dc.contributor.author | Balogun, S.A. | |
dc.date.accessioned | 2020-03-28T16:35:18Z | |
dc.date.available | 2020-03-28T16:35:18Z | |
dc.date.issued | 2012 | |
dc.description.abstract | The phenomenon of anisotropism in most rolled products necessitates that the rolling direction that enhances desirable mechanical property is established. In this paper, the comparative deep drawability of as-received and annealed mild steel containing about 0.1%C was investigated. The flat steel sample was divided into two and classified as as-received and heat treated respectively. The heat treated sample was obtained by annealing at 950˚C after been soaked for 5 hours and deep drawn at ambient temperatures (35˚C - 42˚C). From both samples, circular specimens were machine- blanked parallel to the rolling directions inclined at 0˚, 45˚ and 90˚ respectively and were prepared for deep drawability test while rectangular specimens were prepared for tensile test. Both specimens, as-received and annealed were then subjected to tensile, cupping and microstructural analyses. Results show that the contribution to increased formability at 90° rolling direction seems to have come from the spheroid-like pearlite grains induced during annealing while the stability of spread observed was achieved through a modest increase in strength. Thus, the resistance of annealed eutectoid steel to cupping is quite minimal at 90° to the rolling direction. The desirable drawability characteristics developed by the annealed eutectoid steel specimen are: cup-height, 30 mm maximum and ear, 6.4% maximum. | en_US |
dc.identifier.citation | Adeosun, S.O.; Sekunowo, O.I.; Balogun, S.A. (2012). Investigation into the Deep Drawability of 0.1%C Eutectoid Steel. Journal of Minerals and Materials Characterization and Engineering; 2012(11): 1034-1038 | en_US |
dc.identifier.uri | https://ir.unilag.edu.ng/handle/123456789/8170 | |
dc.language.iso | en | en_US |
dc.publisher | Journal of Minerals and Materials Characterization and Engineering. | en_US |
dc.subject | Eutectoid Steel; Drawability; Annealing; Cupping; Anistropism | en_US |
dc.title | Investigation into the Deep Drawability of 0.1%C Eutectoid Steel | en_US |
dc.type | Article | en_US |